Acrylic iniectio processus corona

Acrylic chemica dicitur polymethyl methacrylate (PMMA in English). Ob defectum PMMA superficies duritiei, facile scalpendi, humilis impulsum resistentia, pauper corona fluidum, etc., modificatio PMMA apparuit unum post alium. Ut copolymerization yl methacrylatae cum styrene et butadiene, permixtionem PMMA ac PC *, etc.

Fluxus PMMA peior est quam PS et ABS, et liquefactio viscositas magis est sensibilis ad mutationes caloris;. Per processus fingens, ad conflandum viscositas maxime mutata est iniectio temperatus. PMMA est polymerum amorphoeum cum temperatura exusta quam 160°C et compositione temperatura 270°C.

1. Plastic processus

PMMA habet quandam aquae effusio, cum aqua effusio rate of * 0.3-0.4%, et humiditas iniectionis corona debet esse infra 0.1%, plerumque 0.04%. Praesentia aquae causa bullae, Gas lineae, et in liquefactum redegit. Ita siccari oportet. Siccus temperatus est 80-90℃, et plus est 3 horae. Recycled materiae potest esse 100% in quibusdam casibus. Ipsam quantum ad necessitatem, qualis pendent, plerumque nimis 30%. Ne pollutio materiae REDIVIVUS, secus perspicuitatem ac proprietates operis effecti afficiet.

Ad

2. Iniectio machinae electio

PMMA nullum speciale requisitum habet ad iniectionem machinarum fingendi. Propter altitudinem ejus liquescat viscositas, altius cochleae sulcus et amplior diametro collium foraminis requiruntur. Si fortitudo facti altior est, cochleae cum longi- tudine ad diametrum rationem adhibendam esse pro low-temperies plasticizationis. Autem, PMMA reponendum est in sicco Hopper.

3. Forma et porta design

The fingunt temperatus esse 60℃-80℃, diametrum principalem debet aequare interiorem cereum, optimus angulus V ° ad VII °, si vis injicere 4mm vel products, angulus erit VII °, et diametri cursoris perveniat 8 ad 10mm *, altiore longitudinem portae non excedunt 50mm. For products with a wall thickness of less than 4mm, the diameter of the runner should be 6-8mm

For products with wall thickness greater than 4mm, the runner diameter should be 8-12mm. Diagonal, fan-shaped and tabular gate depth should be 0.7 to 0.9t (t is the thickness of the product wall), and the diameter of the needle gate should be 0.8 to 2mm; smaller size should be used for low viscosity.

Ad

The common vent holes have a depth of less than 0.05 and a width of 6mm. The demolding angle is between 30′-1° and 35′-1°30° in the cavity part.

Ad

4. Melting temperature

It can be measured by air injection method: ranging from 210°C to 270°C, depending on the information provided by the supplier.

Withdraw the back seat, make the nozzle of the injection molding machine leave the sprue bushing, et manually praestare plasticization iniectio corona, quae est aeris iniectio corona.

5. Iniectio temperatus

Fast iniectio potest esse, sed ne princeps internum accentus, expedit uti multi scaena iniectio, ut tardus-ieiunium tardus, etc., cum injiciendo partes densissimas, utere tardius cursu.

Ad

6. Detentio temporis

Si temperatus est 260° C, commorationis tempus non excedat 10 minuta, et si temperatus est 270° C, commorationis tempus non excedat 8 minuta.