Які матэрыял лепшы для цвілі?

форма для ліцця пад ціскам астуджаецца цвіль meets the requirements of working conditions

1. Зносаўстойлівасць

When the blank is plastically deformed in the mold cavity, it flows and slides along the surface of the cavity, causing violent friction between the surface of the cavity and the blank, which causes the mold to fail due to wear. Таму, the wear resistance of the material is one of the most basic and important properties of the mold.

Цвёрдасць - асноўны фактар, які ўплывае на зносаўстойлівасць. Увогуле, the higher the hardness of the mold parts, the smaller the amount of wear and the better the wear resistance. У дадатак, зносаўстойлівасць таксама залежыць ад тыпу, quantity, форма, памер і размеркаванне карбідаў у матэрыяле.

2. Strength

The working conditions of the molds are mostly very bad, and some of them are often subjected to large impact loads, which leads to brittle fracture. In order to prevent sudden brittle fracture of mold parts during work, the mold must have high strength and toughness.

The toughness of the mold mainly depends on the carbon content, grain size and organization state of the material.

3. Прадукцыйнасць усталостнага разбурэння

In the process of mold work, under the long-term action of cyclic stress, fatigue fracture is often caused. Its forms include low-energy multiple impact fatigue fracture, усталостный разрыў пры расцяжэнні, contact fatigue fracture, and bending fatigue fracture.

The fatigue fracture performance of the mold mainly depends on its strength, цвёрдасць, цвёрдасць, і змест уключэнняў у матэрыял.

4. Прадукцыйнасць пры высокіх тэмпературах

When the working temperature of the mold is higher, the hardness and strength will decrease, leading to early wear of the mold or plastic deformation and failure. Because the mold material should have high anti-tempering stability, to ensure that the mold has a high hardness and strength at the working temperature.

5. Resistance to cold and heat fatigue

Some molds are in a state of repeated heating and cooling during the working process, which causes the surface of the cavity to be pulled and pressure to change the stress, causing surface cracks and peeling, increasing friction, hindering plastic deformation, and reducing dimensional accuracy. Mold failure. Heat and cold fatigue is one of the main forms of failure of hot work molds, and this type of mold should have high resistance to cold and heat fatigue.

6. Ўстойлівасць да карозіі

When some molds such as plastic molds are working, due to the presence of chlorine, fluorine and other elements in the plastics, strong corrosive gases such as hci and hf will be resolved after being heated, which will erode the surface of the mold cavity, increase its surface roughness, and aggravate wear failure.

Па -другое、the mold meets the process performance requirements

The manufacturing of molds generally involves several processes such as forging, cutting, and heat treatment. In order to ensure the quality of mold manufacturing and reduce production costs, the material should have good forgeability, machinability, hardenability, hardenability and grindability; it should also have small oxidation, decarburization sensitivity and quenching Deformation and cracking tendency.

1. Forgeability

It has low hot forging deformation resistance, добрая пластычнасць, wide forging temperature range, low tendency of forging cracking and cold cracking and precipitation of network carbides.

2. Annealing processability

The spheroidizing annealing temperature range is wide, the annealing hardness is low, the fluctuation range is small, and the spheroidizing rate is high.

3. Machinability

The cutting amount is large, the tool loss is low, and the machined surface roughness is low.

4. Sensitivity to oxidation and decarburization

When heated at high temperature, the oxidation resistance is good, the decarburization speed is slow, it is not sensitive to the heating medium, and the tendency of pitting is small.

5. Hardenability

Пасля гашэння, it has uniform and high surface hardness.

6. Hardenability

Пасля гашэння, a deeper hardened layer can be obtained, which can be hardened by using a mild quenching medium.

7. Tendency of quenching deformation and cracking

Conventional quenching has small volume change, shape warping, slight distortion, and low tendency of abnormal deformation. Conventional quenching has low sensitivity to cracking, and is insensitive to quenching temperature and workpiece shape.

8. Grindability

The relative wear of the grinding wheel is small, and the limit of grinding without burn is large. It is not sensitive to the quality of the grinding wheel and cooling conditions, and it is not easy to cause abrasion and grinding cracks.

Па -трэцяе, the mold meets the economic requirements

When selecting матэрыялаў for the цвіль, the principle of economy must be considered to reduce the manufacturing cost as much as possible. Таму, under the premise of satisfying the performance, first choose the lower price, carbon steel can be used without alloy steel, and domestic materials can be used without imported materials. У дадатак, the production and supply of the market should also be considered when selecting materials. The selected steel grades should be as few and concentrated as possible .

The injection molding process conditions have an impact on the appearance and mechanical properties of plastic products. Each process condition parameter affects each other and is not independent. The defects of some products are the result of mutual influence.

Калі ў вас ёсць якія-небудзь пытанні па адносіцца да шчыльнай рабізнай, утворанай ад прамых варот у якасці цэнтра,калі ласка, не саромейцеся пытацца Каманда FLYSE,мы дамо вам самае лепшае абслугоўванне!